Journal
EUROPEAN POLYMER JOURNAL
Volume 49, Issue 7, Pages 1811-1822Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2013.04.007
Keywords
Polyimide-b-polyurea; Block copolymers; Self-assembly; Dielectric constant; Viscoelastic properties; Capacitance
Categories
Funding
- National Science Foundation NSF-CMMI [0758656]
- Office of Naval Research, ONR [N00014-09-1-0980]
- Div Of Civil, Mechanical, & Manufact Inn
- Directorate For Engineering [0758656] Funding Source: National Science Foundation
Ask authors/readers for more resources
A novel type of polyimide (PI)-polyurea (PU) block copolymer containing environmentally friendly aromatic polyether urea was successfully prepared by a two-step polymerization process that produces anhydride terminated poly(4,4'-oxydiphenylene-pyromellitamic acid) and isocyanate terminated poly(4,4'-oxydiphenylene-methylenebisphenylurea) polyurea in the first step followed by coupling of the two homopolymers in the second step to form poly(amic acid)-b-polyurea. The resulting polyimide-b-polyurea copolymer reorganized into a supramacromolecule by formation of hydrogen bonds between adjacent chains. The existence of three types of hydrogen bonds including, inter-urea, urea-methyl and imide-methyl hydrogen bonds was confirmed by using (i) X-ray diffraction (XRD) technique, (ii) Fourier Transform Infrared Spectroscopy (FTIR) and (iii) molecular dynamics simulation. The formation of hydrogen bonds in the copolymers is affected by post-curing temperature and mole fraction of polyurea. Free-standing thin films and coatings of the copolymer of about 70 mu m thickness were prepared by solution casting from N-methyl pyrrolidone, NMP, followed by thermal treatment. The copolymers showed remarkable thermomechanical properties and ultra-low dielectric constant which makes them useful as ionic insulators and anti-corrosion coatings. Increasing polyurea concentration in the copolymers resulted in a significant increase in storage modulus (both in the glassy and rubbery plateau regions), glass transition temperature, T-g and a drastic decrease in dielectric constant. Two glass transition temperatures (T-g) associated with polyimide-rich phase and polyurea-rich phase, respectively, were observed. Damping ability of the copolymers, measured from the area under the alpha-transition peak from the tan delta versus temperature curve, decreased with increasing polyurea concentration. (c) 2013 Elsevier Ltd. All rights reserved.