EUROPEAN POLYMER JOURNAL
Volume 47, Issue 7, Pages 1447-1459Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2011.04.005
Keywords
Morphology development; Dynamic vulcanisation; EPDM gel content; Disintegration; Phase inversion
Categories
Ask authors/readers for more resources
Morphology development and phase inversion were investigated during dynamic vulcanisation of ethylene-propylene-diene terpolymer (EPDM)/polypropylene (PP) blends. The effects of viscosity ratio and cross-linking reactions were also addressed. EPDM/PP blends were dynamically vulcanised in a Haake batch mixer using resole and SnCl2 as cross-linking agents. The morphology development and cross-linking degree with reaction time were followed by morphology analysis (SEM and TEM) and measurement of EPDM gel content, respectively. For the same reaction time, it was found that the EPDM gel content decreased when the low-molecular-weight EPDM was used. As a result, the morphological development was delayed and the phase-inversion point was shifted to higher reaction times, allowing us to monitor morphological development during a thermoplastic vulcanisate (TPV) preparation. Using the low-molecular-weight EPDM and increasing the PP viscosity accelerated the morphological development, shifting phase-inversion to lower reaction times. While blend composition influenced final TPV morphology, it had a minor effect on the mechanism of morphological development. A correlation between cross-linking degree and morphology development was established. The results obtained allowed to propose a mechanism of morphology development during dynamic vulcanisation of the EPDM/PP blends, including phase inversion. (C) 2011 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available