ENGINEERING FAILURE ANALYSIS
Volume 16, Issue 6, Pages 1940-1947Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfailanal.2008.10.013
Keywords
Crankshaft failure; Rotating bending; Steady torsion; Fatigue crack growth; Mixed-mode (I plus III) fracture
Ask authors/readers for more resources
A case study of a catastrophic failure of a web marine crankshaft and a failure analysis under bending and torsion applied to crankshafts are presented. A microscopy (eye seen) observation showed that the crack initiation started on the fillet of the crankpin by rotary bending and the propagation was a combination of cyclic bending and steady torsion. The crack front profile approximately adopts a semi-elliptical shape with some distortion due to torsion and this study is supported by a previous research work already published by the authors. The number of cycles from crack initiation to final failure of this crankshaft was achieved by recording of the main engine operation on board, taking into account the beachmarks left on the fatigue crack surface. The cycles calculated by the linear elastic fracture mechanics approaches showed that the propagation was fast which means that the level of bending stress was relatively high when compared with total cycles of main engine in service. Microstructure defects or inclusion were not observed which can conclude that the failure was probably originated by an external cause and not due to an intrinsic latent defect. Possible effects of added torsional vibrations which induce stresses are also discussed. Some causes are analyzed and reported here but the origin of the fatigue fracture was not clearly determined. (C) 2008 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available