ELECTROCHIMICA ACTA
Volume 89, Issue -, Pages 469-478Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2012.11.091
Keywords
Titania nanorod; Titania nanoparticle; Semiconducting metal oxide electrode; Temperature effect; Dye sensitized solar cell
Categories
Funding
- Academy of Scientific Research and Technology (ASRT)
- Ministry of Scientific Research of Egypt
Ask authors/readers for more resources
A low temperature hydrothermal process have been developed to synthesize titania nanorods (NRs) and nanoparticles (NPs) with controlled size for dye sensitized solar cells (DSSCs). Effect of calcination temperature on the performance of TiO2 nanoparticles for solar cells was investigated and discussed. The crystallite size and the relative crystallinity of the anatase phase were increased with increasing the calcination temperature. The structures and morphologies of both (TiO2 nanorods and nanoparticles) were characterized using XRD, SEM, TEM/HRTEM, UV-vis Spectroscopy, FTIR and BET specific surface area (S-BET) as well as pore-size distribution by BJH. The size of the titania nanorods was 6.7 nm width and 22 nm length while it was 13 nm for nanoparticles. Efficiency of dye-sensitized solar cells (DSSCs) fabricated with oriented TiO2 nanorods was reported to be more superior compared to DSSC based on mesoporous TiO2 nanoparticles due to their high surface area, hierarchically mesoporous structures, low charge recombination and fast electron-transfer rate. With increasing calcination temperature of the prepared nanopowders, the light-electricity conversion efficiency (eta) decreased. The efficiency of the assembly solar cells was decreased due to the agglomeration of the particles and difficulty of electron movement. The power efficiency was enhanced from 1.7% for TiO2 nanoparticles cells at hydrothermally temperature 500 degrees C and 5.2% for TiO2 nanoparticles cells at hydrothermally temperature 100 degrees C to 7.2% for TiO2 nanorods cells under AM1.5 illumination (100 mW cm(-2)). (C) 2012 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available