Journal
ELECTROCHIMICA ACTA
Volume 55, Issue 28, Pages 8709-8716Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2010.08.016
Keywords
Cathode materials; CeO2 coated LiMn2O4; XRD; TEM; Electrochemical performances
Categories
Funding
- University Grants Commission (UGC) New Delhi India
Ask authors/readers for more resources
LiMn2O4 spinel cathode materials were coated with 05 1 0 and 1 5 wt % CeO2 by a polymeric process followed by calcination at 850 degrees C for 6 h in air The surface-coated LiMn2O4 cathode materials were physically characterized using X-ray diffraction (XRD) scanning electron microscopy (SEM) transmission electron microscopy (TEM) and X-ray photoelectron microscopy (XPS) XRD patterns of CeO2-coated LiMn2O4 revealed that the coating did not affect the crystal structure or the Fd3m space group of the cathode materials compared to uncoated LiMn2O4 The surface morphology and particle agglomeration were investigated using SEM TEM image showed a compact coating layer on the surface of the core materials that had average thickness of about 20 nm The XPS data illustrated that the CeO2 completely coated the surface of the LiMn2O4 core cathode materials The galvanostatic charge and discharge of the uncoated and CeO2-coated LiMn2O4 cathode materials were measured in the potential range of 3 0-45 V (0 5 C rate) at 30 C and 60 degrees C Among them the 1 0 wt % of CeO2-coated spinel LiMn2O4 cathode satisfies the structural stability high reversible capacity and excellent electrochemical performances of rechargeable lithium batteries Crown Copyright 2010 Published by Elsevier Ltd All rights reserved
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available