Journal
ELECTROCHIMICA ACTA
Volume 54, Issue 6, Pages 1826-1833Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2008.10.008
Keywords
Fuel cell platinum catalyst degradation; Platinum oxidation and dissolution; Pt ion diffusivity; Relative humidity; Oxygen partial pressure
Categories
Funding
- Toyota Motor Engineering & Manufacturing North America, Inc
Ask authors/readers for more resources
Durability of Pt/C oxygen reduction reaction (ORR) catalyst remains one of the primary limitations for practical application of proton exchange membrane (PEM) fuel cells. In this work, the effects of relative humidity and oxygen partial pressure on platinum catalyst degradation were explored under potential cycling. At 60 degrees C, the loss rates of Pt mass and catalyst active surface area were reduced by about three and two times respectively when the relative humidity was lowered from 100% to 50%. The effects of oxygen partial pressure on cathode degradation were found to be insignificant. Cyclic voltammetry studies showed a slight increase in Pt electrochemical oxidation by water when the humidity increased from 50% RH to 100% RH. The rates of Pt dissolution were only slightly affected by change in humidity, and the accelerated catalyst degradation was ascribed to the increased Pt ion transport in the more abundant and larger water channel networks within the polymer electrolyte. Based on the parametric study results from our previous cathode degradation model, it was estimated that the diffusivity of Pt ions at fully humidified conditions was three times that of the value at 50% RH and 60 degrees C. (C) 2008 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available