Journal
ELECTROCHIMICA ACTA
Volume 55, Issue 1, Pages 31-36Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2009.07.059
Keywords
TiO2; Semiconductor electrode; Water electrolysis; Electrochemical ozone production; Spin-coating
Categories
Ask authors/readers for more resources
An electrode composed of silicon/titanium oxide/platinum/titanium dioxide (Si/TiOx/Pt/TiO2) was fabricated by spin-coating TiO2 multilayers on a Si/TiOx/Pt substrate and was used in electrochemical ozone production (EOP). EOP was realized when the Si/TiOx/Pt substrate was completely covered with the TiO2 film and a current efficiency of 7% was achieved at a low current density of 26.7 mA cm(-2) in 0.01 M HClO4 at 15 degrees C. The TiO2 film was found to be of an anatase-type TiO2 and that to comprise aperture structures from the X-ray diffraction (XRD) and transmission electron microscopy (TEM) observations. Moreover. the fabricated TiO2 film was found to be an n-type semiconductor by photoelectrochemical measurements. The high efficiency at a low current density of EOP on the TiO2 n-type semiconductor was explained to result from the electron transfer through the TiO2/HClO4 interface as tunneling current. When the tunneling current passes through a depletion layer of TiO2, the electrode potential is necessarily high enough to facilitate EOP. (C) 2009 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available