ELECTROCHEMISTRY
Volume 80, Issue 10, Pages 731-733Publisher
ELECTROCHEMICAL SOC JAPAN
DOI: 10.5796/electrochemistry.80.731
Keywords
Li-Air Battery; Air Electrode; Mesoporous Co3O4
Categories
Funding
- New Energy and Industrial Technology Development Organization (NEDO) of Japan
Ask authors/readers for more resources
Mesoporous cobalt oxide (Co3O4) was studied for air electrode of Li-air rechargeable battery. In this study, mesoporous Co3O4 with an average pore radius of 3.09 nm and BET surface area of 99 m(2)/g was successfully prepared by using mesoporous SiO2 for template. Prepared mesoporous Co3O4 was applied for air electrode of Li-air battery after mixing with Pd and it was found that the cell showed a reasonably large discharge capacity of 481 mAh/g(-cat). at 0.1 mA/cm(2) at the initial cycle. Energy efficiency for charge and discharge was estimated to be ca. 75%. Raman spectroscopy suggests that the main product during discharge was Li2O2 and formation of Li2CO3 was hardly observed. C) The Electrochemical Society of Japan, All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available