Journal
CONSTRUCTION AND BUILDING MATERIALS
Volume 23, Issue 2, Pages 687-693Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2008.02.011
Keywords
Phosphogypsum; Building materials; Re-crystallization; Autoclaved; Solid wastes
Categories
Funding
- China Scholarship Council (CSC) [2004842073]
Ask authors/readers for more resources
Previous studies have been carried out on calcined phosphogypsum (PG) for making the building materials. The present study was focused on autoclaved PG and its use in making load-bearing wall bricks. Autoclaved PG was prepared from original waste PG with steam pre-treatment. The crystalline phase, morphology, and thermal characteristics of original waste PG and autoclaved PG were investigated by XRD, SEM, and SDT. Then bricks of the size of Chinese standard brick were prepared from different types of PG in the PG-fly ash-lime-sand system. Results showed that the compressive strength of bricks from autoclaved PG by lower-pressure steam of 0.12 MPa, 120 degrees C for 16 h was much higher. The flexural strength and compressive strength of the bricks could reach 4.0 MPa and 15.0 MPa, respectively. The durability of the bricks was investigated by 15 freezing-thawing cycles at temperatures from -20 degrees C to 20 degrees C, and the weight loss was only 0.029% after all of cycles. Hemihydrates (CaSO4 center dot 0.5H(2)O) were dehydrated products from dihydrates in original PG with lower-pressure steam treatment, and hemihydrates were susceptible to absorbing the humidity and were transformed into densified re-crystallization gypsum (CaSO4 center dot 2H(2)O) that contributed to the final strength of bricks. Microstructural characteristics of bricks were investigated by XRD end SEM. Tobermorite was the significant hydrated product, which contributed to the strength of bricks. The use of autoclaved PG for making load-bearing wall bricks was recommended instead of conventional burnt clay bricks. (C) 2008 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available