Effects of grafted chain length on mechanical and electrical properties of nanocomposites containing polylactide-grafted carbon nanotubes

We herein report the effects of interfacial reinforcement on mechanical and electrical properties of nanocomposites based on polylactide (PLA) and multi-walled carbon nanotube (MWCNT) For this purpose, a series of MWCNTs grafted with PLA chains of various lengths (MWCNT-g-PLAs) were prepared by ring-opening polymerization of L-lactide with carboxylic acid-functionalized MWCNT (MWCNT-COOH). MWCNT-g-PLAs were then mixed with commercial PLA to obtain PLA/MWCNT-g-PLA nanocomposites with 1 0 wt % MWCNT content It was revealed that morphological, mechanical, and electrical properties of PLA/MWCNT-g-PLA nanocomposites were strongly dependent on the PLA chain length of MWCNT-g-PLAs FE-SEM Images exhibited that the nanocomposites containing MWCNT-g-PLA with longer PLA chain length exhibited better dispersion of MWCNTs in the PLA matrix Initial moduli and tensile strengths of PLA/MWCNT-g-PLA composites increased with the increment of chain length of PLA grafted on MWCNTs, which attributes to the improved interfacial adhesion between the grafted PLA chains of MWCNT-g-PLA and the PLA matrix As a result, the experimental initial modulus (2775 +/- 193 MPa) of the nanocomposite including MWCNT-g-PLA with PLA chains of average molecular weight of 530 g/mol was quite close to the theoretical value (2911 MPa) predicted for the nanocomposite with perfect interfacial adhesion. Unexpectedly, electrical resistivities of PLA/MWCNT-g-PLA nanocomposites were found to increase from similar to 10(4) to similar to 10(12) Omega/sq with increasing the PLA chain length of MWCNT-g-PLA, which is due to the fact that the PLA chains grafted on MWCNTs prevent the formation of the electrical conduction path of MWCNTs in the PEA matrix (C) 2010 Elsevier Ltd All rights reserved