Journal
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING
Volume 39, Issue 5, Pages 761-768Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.compositesa.2008.02.006
Keywords
polymer matrix composites (PMCs); mechanical properties; thermal properties; micro-mechanics
Ask authors/readers for more resources
Fumed silica particles with average primary particle diameters of 12 and 40 nm were combined with a low viscosity bisphenol E cyanate ester resin to form composite materials with enhanced storage modulus and reduced damping behavior, as evidenced by dynamic mechanical analysis (DMA). The storage modulus increased with volume fraction of fumed silica in both the glassy and rubbery regions, but the increase was more pronounced in the rubbery region. The maximum increase in storage modulus in the glassy region was 75% for 20.7 vol% of 40 nm fumed silica, while the same composition showed a 231% increase in the rubbery storage modulus. Furthermore, decreases in damping behavior were used to estimate the effective polymer-particle interphase thickness. The glass transition temperature of the nanocomposites was not changed significantly with increasing volume fraction. (C) 2008 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available