Keywords
Core-shell; Mesoporous; Stober; Superparamagnetic; Titania
Categories
Funding
- National Science Foundation of China [30930028]
- PRC [2011CB707700]
- Major International (Regional) Joint Research Program of China [81120108013]
- National Science Foundation for Post-doctoral Scientists of China [20100480030]
- Shanghai Postdoctoral Sustentation Fund [11R21411500]
Ask authors/readers for more resources
We demonstrate a novel synthesis of sandwich structured superparamagnetic mesoporous microspheres with a silica-coated magnetite core and mesoporous titania shell using a block-copolymer-templating approach. The synthesis process is simple and facile, in which uniform magnetite particles were coated with silica through classical Stober method. And then, a mesostructured P123/TiO2 composite was deposited on the silica-coated magnetite core by using Pluronic P123 block-copolymer as a template and tetrabutyl titanate (TBOT) as a precursor in ethanol aqueous solution. After calcination at 400 degrees C, the superparamagnetic microspheres with crystallized mesoporous titania shell were obtained. The sandwich structures of the obtained composite microspheres have been confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). The TEM and SEM images show that the microspheres possess a uniform diameter of similar to 420 nm and a homogeneous mesoporous shell of similar to 40 nm. The XRD indicates that mesoporous shell is highly crystallized anatase titania. The obtained microspheres possess tunable specific surface areas of 50-100 m(2)/g, and controlled large mesopore sizes of 3.7-5.0 nm. Furthermore, the resulting superparamagnetic microspheres with a high saturation magnetization value of similar to 34 emu/g could be enriched completely within 10 s under the application of a 0.2 T magnet. (c) 2012 Elsevier B.V. All rights reserved.