Keywords
M-type hexaferrites; Pr-substitution; Sol-gel; Microstructure; M-H loops
Funding
- Department of Physics, B.Z. University Multan
Ask authors/readers for more resources
A series of M-type hexaferrites with chemical formula Ba0.25Sr0.75PrxFe12-xO19 (x=0.00, 0.05, 0.10, 0.15, 0.20, 0.25) were synthesized using sol-gel autocombustion method. The samples were pre-sintered at a temperature of 800 degrees C for 3 h and were finally sintered at 1200 degrees C for 1 h at the heating rate of 10 degrees C/min. The thermal properties of the specimen have been investigated by thermogravimetric and differential thermal analyses. The structures and micrographs of the samples were systematically examined by X-ray diffraction and scanning electron microscopy, respectively. Vibrating sample magnetometer was also used in order to study the magnetic parameters of these ferrites. The hard magnetic behavior was confirmed by M-H loops for all the samples except for the sample with x=0.10 concentration which exhibits maximum saturation magnetization (M-s) and a few hundred oersteds of coercivity (H-c). Thus high M-s and low H-c cause to increase the permeability of the sample which is favorable for impedance matching in microwave absorption. (C) 2014 Elsevier B.V. All rights reserved,
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available