Synthesis of 10nm-NaYF4:Yb,Er/NaYF4 Core/Shell Upconversion Nanocrystals with 5nm Particle Cores

A new method is presented for preparing gram amounts of very small core/shell upconversion nanocrystals without additional codoping of the particles. First, ca. 5nm -NaYF4:Yb,Er core particles are formed by the reaction of sodium oleate, rare-earth oleate, and ammonium fluoride, thereby making use of the fact that a high ratio of sodium to rare-earth ions promotes the nucleation of a large number of -phase seeds. Thereafter, a 2nm thick NaYF4 shell is formed by using 3-4nm particles of -NaYF4 as a single-source precursor for the -phase shell material. In contrast to the core particles, however, these -phase particles are prepared with a low ratio of sodium to rare-earth ions, which efficiently suppresses an undesired nucleation of -NaYF4 particles during shell growth.