Controlled degradation of polypropylene (PP) by peroxide was carried out in a laboratory twin-screw extruder ZSK 18 and the change in Molecular Weight Distribution (MWD) was measured using Size Exclusion Chromatography-Differential Viscosimetry (SEC-DV). The MWD results were compared to MWD predictions from a kinetic model developed and validated in earlier work (Iedema et al., 2001) assuming ideal mixing. Clear deviations were observed - the measured MWD was broader - that could only be explained by unaccounted heterogeneity in the extruder. Incorporating the relatively narrow Residence Time Distribution (RTD) in the twin-screw extruder did not lead to MWD broadening. In contrast, the exponential RTD of a Continuously Stirred Tank Reactor (CSTR) yielded a MWD widening that was too extreme. A new micromixing model, based on the striation thinning model by Ottino (1980), was constructed partly based on Monte Carlo sampling using a monomer scission probability (Tobita, 1996). This model was adapted to the geometry of the extruder entrance and the peroxide feed practice consisting of introducing a few per thousand peroxide-rich PP particles among pure PP particles. This micromixing model indeed allowed obtaining very good matches between measured and modeled MWD. Under different experimental conditions with respect to initial PP quality and amount of peroxide added, with a constant value for the striation thinning parameter the errors between measured and predicted MWD were around 5%. (C) 2011 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available