The tensile strength and elongation at break of epoxidized natural rubber (ENR) blended with natural rubber (NR) was studied. ENR 25, ENR 50, and one grade of natural rubber (SMR L) were used as the elastomers- The composition of ENR was varied from 0% to 100% rubber. The accelerated sulfur vulcanization system was used throughout the investigation. The tensile property of una,oed and aged samples, was determined by using the Monsanto tensometer (T10) operating at 50 cm/min. Results show that the tensile strength and elongation at breakpasses through a maximum at 50% ENR for both ENR25/SMR L and ENR50/SMR L blends. This positive deviation from ideality is attributed to the mutual reinforcement of ENR and NR in the blends as a result of strain-induced crystallization. This synergistic effect is more pronounced in the case of ENR 25 due to the higher crystallinity and availability of more double bonds, which is more compatible:to NR compared to ENR 50/NR blends. For the aged samples, a drop in the tensile property associated to the breakdown of the polysulfidic cross-link during:aging is observed. A systematic study of the effect of sulfur concentration on the percentage retention of tensile property of the ENRblends after aging reveals that percentage retention decreases with increasing sulfur loading, which, in turn, enhances the formation of the polysulfidic cross-link; thus, more breakdown is observed in the rubber vulcanizate.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available