Journal
JOURNAL OF MATERIALS SCIENCE
Volume 36, Issue 24, Pages 5757-5765Publisher
KLUWER ACADEMIC PUBL
DOI: 10.1023/A:1012939601936
Keywords
-
Categories
Ask authors/readers for more resources
Steels in which Cu content was altered from 0 to 1.5 mass% were subjected to various heat treatments to change the state of Cu. Concerning these respective steels, fatigue ratio by a stress controlled fatigue test and fatigue resistance by a strain controlled fatigue test thereof were compared. Furthermore dislocation substructure and surface defect during and after cyclic straining were investigated to clarify the effect of Cu on fatigue properties. The fatigue ratios at 2.0 x 10(6) loading cycles of the Cu added steels after aged at 450 and 750 degrees C are 0.7, remarkably high as compared with those of the Cu added steels after aged at 550 and 650 degrees C, the Cu free steels and any other conventional steels whose fatigue ratio are approximately between 0.5 and 0.6. The fatigue resistance of the as-rolled Cu added steel maintains steady cyclic hardening until fracture. To the contrary the Cu added steel after heat treatment at 550 degrees C shows cyclic hardening to the peak stress and then shows a cyclic softening until fracture. The surface roughness of the Cu added steels after cyclic straining are relatively shallow compared with those of the Cu free steel. The internal substructure of the Cu free steel shows typical cell structure but those of the Cu added steels exhibit vein structure. (C) 2001 Kluwer Academic Publishers.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available