Journal
COMPOSITES SCIENCE AND TECHNOLOGY
Volume 61, Issue 2, Pages 301-310Publisher
ELSEVIER SCI LTD
DOI: 10.1016/S0266-3538(00)00222-0
Keywords
hydroxyapatite; zirconia; composite; microstructure; mechanical properties
Categories
Ask authors/readers for more resources
Hydroxyapatite is the mineral component of natural hard tissues and, as such, it has been studied extensively as a candidate biomaterial for its use in prosthetic applications. However. the main weakness of this material lies in its poor mechanical strength which makes it unsuitable for load-bearing applications. On the other hand, partially stabilized zirconia has been widely studied on account of its high strength and fracture toughness, and good biocompatibility. Therefore, it is believed that the addition of a particulate zirconia phase to a hydroxyapatite one may lead to an improvement of the mechanical properties of this kind of composite and will not affect its biocompatibility. In this study, two series of zirconia- hydroxyapatite composites, Z4H6 and Z6H4 with 40 and 60 vol.% of zirconia content respectively, were prepared by powder uniaxial pressing at 700 MPa and sintering in air at 120-1500 degreesC for 3 h. The sintering behavior. microstructural characteristics and mechanical properties were evaluated. Variation of average grain size for the zirconia and hydroxyapatite phases with sintering temperature was observed. Relative densities ranging from 89 to 91% of the theoretical values were reached for the Z6H4 ceramic series and for the Z4H6 sample sintered at 1400 degreesC, although microcracks were present in all specimens sintered at 1400 and 1500 degreesC. Values of ultimate compressive strength, Young's modulus. micro-Vickers hardness and Poisson's ratio near to those for human cortical bone and human tooth (dentine and enamel) were found for almost all samples investigated suggesting that these materials present potential applications as structural implants. (C) 2001 Elsevier Science Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available