Journal
CERAMICS INTERNATIONAL
Volume 39, Issue 1, Pages 457-462Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2012.06.048
Keywords
Cadmium titanate; Nanofibers; Humidity sensor; Response time
Categories
Funding
- Higher Education Commission (HEC), Pakistan
Ask authors/readers for more resources
We report humidity sensing characteristics of CdTiO3 nanofibers prepared by electrospinning. The nanofibers were porous having an average diameter and length of similar to 50-200 nm and similar to 100 mu m, respectively. The nanofiber humidity sensor was fabricated by defining aluminum electrodes using photolithography on top of the nanofibers deposited on glass substrate. The performance of the CdTiO3 nanofiber humidity sensor was evaluated by AC electrical characterization from 40% to 90% relative humidity at 25 degrees C. The frequency of the AC signal was varied from 10(-1) to 10(6) Hz. Fast response time and recovery time of 4 s and 6 s were observed, respectively. The sensor was highly sensitive and exhibited a reversible response with small hysteresis of less than 7%. Long term stability of the sensor was confirmed during 30 day test. The excellent sensing characteristics prove that the CdTiO3 nanofibers are potential candidate for use in high performance humidity sensors. (c) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available