Journal
CERAMICS INTERNATIONAL
Volume 38, Issue 2, Pages 973-979Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2011.08.018
Keywords
Magnetic properties; Nano-crystalline strontium hexaferrite; Chemical preparation
Categories
Ask authors/readers for more resources
Nano-crystalline strontium hexaferrite (SrFe12O19) powder was synthesized using the classical co-precipitation and microemulsion methods. The precursors were obtained by precipitating Sr2+ and Fe2+ ions using tetramethylammonium hydroxide and calcinating at different temperatures ranging from 400 degrees C to 1000 degrees C in air. The influence of the Sr2+/Fe3+ mol ratio and the calcination temperature on the product formation and magnetic properties were studied. The formation of nanosized particles of SrFe12O19 with a relatively high saturation magnetization M-s = 64 Am-2/kg, remanent magnetization of M-r = 39 Am-2/kg and a coercitivity of H-c = 5.5 kOe was achieved at a Sr2+/Fe3+ mol ratio of 1:8 calcined at 900 degrees C. The formation of the (SrFeO19)-O-12 was inspected using XRD analysis, thermogravimetric analysis (TGA), differential thermal analysis (DTA), TEM, and magnetic measurements. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available