Volume 34, Issue 4, Pages 583-590Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.cemconcomp.2011.08.013
Keywords
Blast furnace slag; Compressive strength; Mix design method; Self-compacting concrete; Superplasticizers; Workability
Ask authors/readers for more resources
This paper presents the results of an experimental investigation carried out to study the effect of granulated blast furnace slag and two types of superplasticizers on the properties of self-compacting concrete (SCC). In control SCC, cement was replaced with 10%, 15%, 20%, and 25% of blast furnace slag. Two types of superplasticizers: polycarboxylate based superplasticizer and naphthalene sulphonate based superplasticizers were used. Tests were conducted for slump flow, the modified slump test, V-Funnel, J-Ring, U-Box, and compressive strength. The results showed that polycarboxylate based superplasticizer concrete mixes give more workability and higher compressive strength, at all ages, than those with naphthalene sulphonate based superplasticizer. Inclusion of blast furnace slag by substitution to cement was found to be very beneficial to fresh self-compacting concrete. An improvement of workability was observed up to 20% of slag content with an optimum content of 15%. Workability retention of about 45 min with 15% and 20% of slag content was obtained using a polycarboxylate based superplasticizer; compressive strength decreased with the increase in slag content, as occurs for vibrated concrete, although at later ages the differences were small. (C) 2011 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available