Journal
CELLULOSE
Volume 25, Issue 10, Pages 6083-6092Publisher
SPRINGER
DOI: 10.1007/s10570-018-1969-y
Keywords
Colloidal charge; Recycled paper; Polyelectrolytes; Poly(allylamine hydrochloride); Polyacrylic acid; Cellulosic nanomaterials
Ask authors/readers for more resources
A novel procedure based on the addition of polyelectrolyte complexes (PECs) onto the pulp containing lignocellulosic micro/nanofibers (LCMNF) is presented. This procedure allows increasing paper strength avoiding an excessive loss in drainability. LCMNF were obtained from partially delignified kraft pine sawdust using a high-pressure homogenizer. Cationic complexes (CatPECs) were prepared by adding the anionic polyelectrolyte solution (polyacrylic acid) on the cationic polyelectrolyte solution (poly(allylamine hydrochloride)). According to turbidity and surface morphology changes, an interaction between CatPECs and LCMNF could be established. Different CatPEC dosages (from 0.3 to 1.0% on pulp) were added on a recycled unbleached softwood kraft pulp containing 3% of LCMNF. For a PEC dosage of 0.75% on pulp, an optimum balances between negatively and positively charged materials [near to zero value of the logarithm of the colloidal titration ratio (logCTR)] was found. Britt Dynamic Drainage Jar test showed a high retention of fines and LCMNF for all PEC dosages. A maximum in retention value was obtained for the addition of 0.75% of PECs on pulp, dosage that was suggested as optimum by the logCTR. In addition, the best drainability value (18A degrees SR) was obtained for this PEC addition level. Papermaking properties were clearly improved for all dosage of PECs. Particularly for a dosage of 0.75% of PECs on pulp, tensile strength was noticeably increased (+48%) and both compressive resistance Concora Medium Test (CMT) and Short-span Compressive Test (SCT) were markedly increased (+64% and +39%, respectively). These results suggest that PECs are a possible alternative to assist the application of LCMNF in papermaking.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available