ISIJ INTERNATIONAL
Volume 44, Issue 6, Pages 1103-1107Publisher
IRON STEEL INST JAPAN KEIDANREN KAIKAN
DOI: 10.2355/isijinternational.44.1103
Keywords
thermal fatigue; cast hot work die steel; crack initiation and propagation; oxidation and temper resistances
Categories
Ask authors/readers for more resources
The thermal fatigue (TF) behavior of a new type high-Cr cast hot work die steel was investigated. The results indicate that TF cracks initiate at the grain boundaries or at the interface between inclusion and matrix, which had been oxidized, and then propagated along the grain boundaries. The thermal fatigue crack initiation and propagation have been accelerated greatly by oxidation. The new type cast high Cr hot work die steel has a better thermal fatigue resistance compared to 4Cr5MoSiV1(8407) steel under thermal cycling temperatures of 650-25degreesC. Good oxidation and temper resistances are the main causes for the better TF resistance of the new type high-Cr cast hot work die steel.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available