CERAMICS INTERNATIONAL
Volume 33, Issue 7, Pages 1399-1402Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2006.04.018
Keywords
sintering; grain size; mechanical properties; Ti3AlC2
Categories
Ask authors/readers for more resources
The effect of silicon on synthesis of Ti3AlC2, by spark plasma sintering (SPS) from TiC/Ti/Al powders was investigated. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used for phase identification and microstructure evaluation. The results showed that addition of silicon can considerably accelerate the synthesis reaction of Ti3AlC2 and fully dense, essentially single-phase polycrystalline Ti3AlC2 could be successfully obtained by sintering 2TiC/1Ti/1Al/0.2Si powders at 1200-1250 degrees C under a pressure of 30 MPa. SEM micrographs showed the obtained Ti3AlC2 samples to be about 2-5 mu m thick and 10-25 mu m long platelets. The fracture toughness and flexural strength of Ti3AlC2, were 7.0 +/- 0.2 MPa m(1/2) and 450 +/- 10 MPa, respectively. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available