Journal
JOURNAL OF BIOMATERIALS SCIENCE-POLYMER EDITION
Volume 18, Issue 4, Pages 353-368Publisher
VSP BV
DOI: 10.1163/156856207780425013
Keywords
atomic force microscopy; poly(urethane urea); polyurethane; nanoscale indentation; surface characterization
Ask authors/readers for more resources
Atomic force microscopy utilizing both tapping mode and force mode imaging is used to visualize the separated microphases in poly(urethane urea) films under ambient and aqueous conditions. The topography of the PUU surface changed upon hydration with the formation of nanometer-sized features on the surface. The surface becomes enriched in hard domains with hydration time and this enrichment is irreversible after dehydration. Force mode measurements were used to quantify mechanical properties as both indentation and modulus measurements. Analysis of the modulus during indentation reveals the three-dimensional nature of the structures, with the surface being covered by a 2-20-nm-thick soft segment overlayer under ambient conditions, while hydration leads to the loss of this overlayer. The force measurements also reveal the presence of regions having modulus values between those of the hard and soft phases and located spatially near the interface between the hard and soft domains. However, such regions with intermediate modulus were only rarely seen following hydration. Calculation of the Young's modulus from the compression data shows that hydration increases the modulus of the PUU surface by both enrichment of the amount of hard domain present and increasing the modulus of the individual hard and soft phases themselves. Direct visualization of the distribution of these different domains on the surface by nanoscale measurements provides an important path to characterizing the relationships between the surface properties of these materials and subsequent performance in biomedical applications.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available