Journal
JOURNAL OF COLLOID AND INTERFACE SCIENCE
Volume 458, Issue -, Pages 155-159Publisher
ACADEMIC PRESS INC ELSEVIER SCIENCE
DOI: 10.1016/j.jcis.2015.07.045
Keywords
Green synthesis; Silver nanowires ink; Clove oil; Room temperature; Conductivity; Seed free method; Nanoelectrode; Optoelectronic; HR-TEM
Categories
Funding
- PSG son's and charities
Ask authors/readers for more resources
Hypothesis: Silver nanowires (AgNWs) have been demonstrated to be a promising next generation conducting material and an alternative to the traditional electrode (ITO) because of its high conductivity, transparency and stability. Generally. AgNWs are synthesized by chemical method (mainly polyol reduction method) at high temperature in the presence of exotic seeds. The present work aims at the green approach for preparation and characterization of 1D AgNWs ink using clove oil (Syzygium Aromaticum) at room temperature. Experiments: AgNWs was prepared by green synthesis using clove oil as reducing as well as capping agent at room temperature. The obtained ink was purified, filtered and redissolved in methanol. Findings: The prepared AgNWs showed an absorption peaks at 350 and 387 nm in the UV-vis spectrum due to transverse SPR mode of silver. From the HR-TEM analysis, it was observed that the AgNWs possess an average diameter and length of similar to 39 +/- 0.01 nm and similar to 3 mu m, respectively. The obtained AgNWs are crystalline in nature and are arranged in a perfect crystal lattice orientation, which was confirmed from the selected area electron diffraction studies. Moreover, the X-ray diffraction analysis confirms the face centered cubic structure. The AgNWs coated glass substrate shows an electrical conductivity of similar to 0.48 x 10(6) S/m. (C) 2015 Elsevier Inc. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available