Journal
BIOMATERIALS
Volume 31, Issue 6, Pages 1260-1269Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.biomaterials.2009.11.005
Keywords
Hierarchically porous scaffolds; Magnesium calcium phosphate; Biodegradability; Biocompatibility; Bone generation
Funding
- National Natural Science Funds of China [30970720]
- Nano special program of Science and Technology Development of Shanghai [0852nm02700]
- Standard Special program of Science and Technology Development of Shanghai [08DZ0501600]
- 973Project of the Ministry of Science and Technology of the People's Republic of China [2007CB936103]
- Shanghai Pujiang Program (2008)
Ask authors/readers for more resources
Hierarchically 3D microporous/macroporous magnesium-calcium phosphate (micro/ma-MCP) scaffolds containing magnesium ammonium phosphate hexahydrate [NH4MgPO4 center dot 6H(2)O] and hydroxyapatite [Ca-10(PO4)(6)(CH)(2)] were fabricated from cement utilizing leaching method in the presence of sodium chloride (NaCl) particles and NaCl saturated water solution. NaCl particles produced macropororosity, and NaCl solution acted as both cement liquid and porogens, inducing the formation of microporosity. The micro/ma-MCP scaffolds with porosities varied from 52 to 78% showed well interconnected and open macropores with the sizes of 400-500 mu m, and degradation of the scaffolds was significantly enhanced in Tris-HCl solution compared with macroporous MCP (ma-MCP) and corresponding calcium phosphate cement (CPC) scaffolds. Cell attachment and proliferation of MG(63) on micro/ma-MCP were significantly better than ma-MCP and CPC scaffolds because of the presence of microporosity, which enhanced the surface area of the scaffolds. Moreover, the alkaline phosphatase (ALP) activity of the MG(63) cells on micro/ma-MCP was significantly higher than ma-MCP and CPC scaffolds at 7 days, and the MG(63) cells with normal phenotype spread well and formed confluent layers across the macroporous walls of the microlma-MCP scaffolds. Histological evaluation confirmed that the micro/ma-MCP scaffolds improved the efficiency of new bone regeneration, and exhibited excellent biocompatibility, biodegradability and faster and more effective osteogenesis in vivo. (C) 2009 Elsevier Ltd. All rights reserved.