Analysis of the NiCo2O4 spinel surface with Auger and X-ray photoelectron spectroscopy

Nickel cobaltite, NiCo2O4, has been synthesized by sol-gel and thermal decomposition techniques and the surface composition studied with Auger (AES) and X-ray photoelectron spectroscopies (XPS). The as-introduced samples are near-stoichiometric, although samples fabricated by thermal decomposition tend to be oxygen-deficient by approximately 25% of the predicted spinel concentration. Nickel 2p XPS indicates the predominant form of the metal to be Ni2+, with the cations located in octahedral sites. The cobalt cations are equally divided between tetrahedral and octahedral sites as Co3+ The oxygen XP Is spectrum is composed of two peaks, the main lattice peak at 529.6 eV and a component at 531.2 eV with about 40% of the total O Is intensity in stoichiometric samples. While the possibility of hydroxyl contaminants cannot be discounted, most of the intensity in the 531.2 eV peak is believed to be intrinsic to the NiCo2O4, surface. Heating the cobaltite in ultrahigh vacuum (UHV) results in surface reduction, with the largest changes apparent in the Co 2p XP spectrum, which shows clear signs of reduction to octahedral Co2+. Changes brought about by the reduction are not reversible, and although it is possible to reoxidize the material, the surface undergoes phase separation to Co3O4 and NixCo1-xO. (C) 2000 Published by Elsevier Science B.V.