Journal
PHYSICAL REVIEW B
Volume 62, Issue 11, Pages 7527-7534Publisher
AMER PHYSICAL SOC
DOI: 10.1103/PhysRevB.62.7527
Keywords
-
Ask authors/readers for more resources
The interaction of potassium atoms on top of Cr2O3(0001)/Cr(110) has been studied using work-function (Delta phi), temperature programmed desorption (TPD), and optical second-harmonic generation (SHG) measurements. Potassium grows via the completion of a first layer, followed by a second layer in the form of two-dimensional (2D) islands, and at higher coverage 3D clusters are formed. This growth model is supported by and consistent with the results obtained from all three methods. Work-function data suggest that annealing at temperatures above 350 K results in the formation of a surface potassium oxide compound, provided the potassium coverage is higher than 0.5 monolayers (ML). Diffusion of alkali-metal atoms on an oxide surface is reported here over distances of several micrometers. This was measured using optical SH diffraction from coverage gratings that were generated by laser-induced thermal desorption. The activation energy for surface diffusion of potassium on Cr2O3(0001)/Cr(110) has been determined to be 11+/-0.5 kcal/mol with a preexponential factor D-0=10(5) cm(2)/sec in the coverage range of 1.5-2.5 ML, dropping to 9 kcal/mol and D-0=3 X 10(3) cm(2)/sec at a coverage of 3.0 ML. These results are consistent with the diffusion of atoms in the third layer, on top of two-dimensional potassium islands in the second layer, the activation energy represent the barrier for descending from the 2D islands.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available