JOURNAL OF NUCLEAR MATERIALS
Volume 288, Issue 2-3, Pages 222-232Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/S0022-3115(00)00723-6
Keywords
-
Ask authors/readers for more resources
The service-exposed (similar to 60 000 h/873 K) Alloy 625 ammonia cracker tubes showed higher strength and lower ductility compared to the virgin material in the solution annealed state. Precipitation of intermetallic gamma and Ni-2(Cr,Mo) phases and the inter and intragranular carbides were found to be responsible for higher strength of the service-exposed alloy. Subjecting the service-exposed alloy to thermal aging treatments subsequently at 923 It and 1123 It (above the service temperature of the exposed alloy) led to the dissolution of the intermetallic phases that in turn increased the ductility of the alloy. Post-service aging of the alloy at 923 K for short durations resulted in the dissolution of the Ni-2(Cr,Mo)phase. The dissolution of the Ni-2(Cr,Mo)-phase exhibited significant influence upon yield strength OCS) but negligible effect on ductility. Prolonged aging of the alloy for 500 h at 923 K resulted in the precipitation of intermetallic F-phase. Post-service aging of the alloy at 1123 K promoted the dissolution of both Ni-2(Cr,Mo) and gamma formed during service. Longer duration aging at the same temperature led to the precipitation of the delta -phase with an associated increase in strength and loss in ductility. Re-solution annealing of the service-exposed alloy at 1423 K caused the dissolution of the strengthening phases. When the re-solution annealed alloy was subjected to prolonged exposure at 923 K, the yield stress was found to increase rapidly with aging time with attendent loss in ductility due to the precipitation of gamma . (C) 2001 Elsevier Science B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available