JOURNAL OF NON-CRYSTALLINE SOLIDS
Volume 285, Issue 1-3, Pages 90-95Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/S0022-3093(01)00437-9
Keywords
-
Ask authors/readers for more resources
Porous TiO2 thin films have potential applications in optical-, electronic- and mechanical-components, catalysts, photoelectrodes, etc. A novel method to control pore sizes of sol-gel thin films by surfactant templating was investigated. The coating sol was obtained by hydrolysis of Ti(C4H9O)(4) in ethanol solution. The films were prepared by spin-coating on glass substrates and drying at 90 degreesC (xerogel film) or drying after immersion in a cetyltrimethylammoniumchloride (CTAC) or benzyltrimethylammoniumchloride solution for 1-24 h (CTAC- or BTAC-modified him), followed by calcination at 500 degreesC in air. The calcined films were transparent and 30-120 nm in thickness. The refractive indices of the CTAC- and BTAC-modified films were about 1.7 and 1.9, respectively. These were 10-20% lower than those of the xerogel films. A columnar structure was observed by SEM and AFM. The columns were about 30 nm in diameter. The spacing between the columns was about 10 nm, corresponding to the size of CTAC micelles. These results show that the microstructure and pore size of the sol-gel films can be controlled by the surfactant-templating. (C) 2001 Elsevier Science B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available