Journal
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
Volume 24, Issue 12, Pages 781-790Publisher
WILEY
DOI: 10.1046/j.1460-2695.2001.00459.x
Keywords
bearing steel; fish eye; high cycle fatigue; internal crack; non-metallic inclusion; S-N curve; surface crack
Ask authors/readers for more resources
The S-N curve obtained from cantilever-type rotary bending fatigue tests using hourglass-shaped specimens of high carbon-chromium bearing steel clearly distinguished the fracture modes into two groups each having a different crack origin. One was governed by crystal slip on the specimen surface, which occurred in the region of short fatigue life and a high stress amplitude level. The other was governed by a non-metallic inclusion at a subsurface level which occurred in the region of long fatigue life and low stress amplitude. The inclusion developed a fish-eye fracture mode that was distributed over a wide range of stress amplitude not only below the fatigue limit defined as the threshold for fracture due to the surface slip mode but also above the fatigue limit. This remarkable shape of the S-N curve was different from the step-wise one reported in previous literature and is characterized as a duplex S-N curve composed of two different S-N curves corresponding to the respective fracture modes. From detailed observations of the fracture surface and the fatigue crack origin, the mechanisms for the internal fracture mode and the characteristics of the S-N curve are discussed.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available