Specular spin-valve films with an FeCo nano-oxide layer by ion-assisted oxidation

We compared the specular spin-valve films with an Fe50Co50 nano-oxide layer (NOL) and a Co90Fe10 NOL in a pinned layer, prepared by natural oxidation (NO) and ion-assisted oxidation (IAO). For the IAO, an Ar-ion beam was used for the energy-assist effect during the oxidation, resulting in thermally stable NOL formation. With small oxygen exposures during the oxidation for the Fe50Co50 NOL by IAO, good ferromagnetic coupling through the NOL and high specularity at the NOL interface were concurrently obtained. Moreover, twisted coupling through the NOL was observed for the Fe50Co50 NOL by IAO for higher oxygen exposures. On the other hand, the NO did not cause large magnetoresistance (MR) enhancement for either the Co90Fe10 or Fe50Co50 NOLs, and the Co90Fe10 NOL by IAO caused weak magnetic coupling through the NOL, resulting in a small MR ratio. The Fe50Co50 NOL for small oxygen exposures is a good candidate for a final specular spin-valve film head for 100-Giga-bit per square inch recording. (C) 2002 American Institute of Physics.