Thin films of nickel oxide (NiO) were deposited on Corning 7059 glass substrates by RF magnetron sputtering. The relationship between substrate temperature and resistivity and the microstructural defects of the NiO films were investigated. Crystalline NiO film with (111) orientation was obtained in this study. A resistivity of 0.22 Ohm cm and a hole concentration of 4.4 X 10(19) cin' were obtained for non-doped NiO films prepared at a substrate temperature of 300 degreesC in pure oxygen sputtering gas. As the substrate temperature was increased from 300 to 400 degreesC, the resistivity changed from 0.22 to 0.70 Ohm cm. The mechanism of electrical conductivity for the NiO films is discussed from the viewpoint of defect chemistry and was confirmed by X-ray photoelectron (XPS) and energy-dispersive spectroscopy (EDS), and X-ray diffraction (XRD) data. (C) 2002 Elsevier Science B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available