APPLIED SURFACE SCIENCE
Volume 195, Issue 1-4, Pages 107-116Publisher
ELSEVIER
DOI: 10.1016/S0169-4332(02)00552-4
Keywords
reactive ion etching; tetrahedral amorphous carbon film; metal containing carbon films; filtered cathodic vacuum arc deposition; reactive ion beam etching
Ask authors/readers for more resources
A preliminary study on the etching behaviour of pure and metal containing amorphous carbon (a-C) films has been studied using reactive ion etching (RIE) as well as reactive ion beam etching (RIBS). The RIE etching of a-C films, prepared from pure and 1 at.% Al containing carbon cathodes, displays a significant increase in etching rate with increase in discharge power. The inclusion of even a small percentage of metal causes a drastic reduction in the etching rate. The films that contain higher percentages of metal become more difficult to etch using RIE with oxygen plasma. Therefore, etching of the samples by RIBE technique using a plasma mixture of oxygen and argon has been carried out. A significant reduction in the etching rate with increasing metal content was observed for both Al and Ti containing a-C films. This led us to try etching of Ti containing a-C films by RIE technique using a plasma mixture of CF4 and oxygen. The result shows that the etching rate increases with increasing Ti content. The analysis of the etched surfaces measured by visible Raman indicates that all the surfaces remain almost the same regardless of the processes undergone. However, the morphology measured using Atomic Force Microscopy (AFM) shows that the surface roughness increases significantly after etching, especially for the pure carbon films. (C) 2002 Elsevier Science B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available