Journal
BIOMATERIALS
Volume 23, Issue 24, Pages 4731-4737Publisher
ELSEVIER SCI LTD
DOI: 10.1016/S0142-9612(02)00222-3
Keywords
abrasion; hydroxyapatite coatings; thermal spraying; roughness; weight loss
Ask authors/readers for more resources
The surface condition of hydroxyapatite thermal sprayed coatings can be measured in terms of smooth melted and unmelted regions. Both these areas collectively contribute to abrasion resistance of a coated implant. The purpose of this work was to determine the influence of abrasion on the surface characteristics of coatings. Coatings with three degrees of roughness (R,, of 7, 10 and 24 mum) were produced by thermal spraying. These coatings were subjected to abrasion in a pin-on-disk test. It was found that the majority of weight loss occurs within the first minute of the abrasion. Raised areas from the coating are removed and the bone analogue pin spreads amongst the elevated areas to produce a smoother coating. Further, abrasion is dependent upon the applied load. Small loads produce a smaller or negligible increase in coating loss, however, a higher load is able to displace more material from the coating surface. It is expected that the coating loss from plasma sprayed coatings amounts to a value of less than 3 wt% during the insertion into bone. Modification of the coating surface from abrasion is dependent upon the surface roughness of the coating. (C) 2002 Elsevier Science Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available