Preparation of 5-fluorouracil-loaded poly(L-lactide-co-glycolide) wafer and evaluation of in vitro release behavior

The controlled delivery of anticancer agents using biodegradable polymeric implant has been developed to solve the problem of penetration of blood brain barrier and severe systemic toxicity. This study was performed to prepare 5-FU-Ioaded poly(L-lactide-co-glycolide) (PLGA) wafer fabricated microparticles prepared by two different method and to evaluate their release profile for the application of the treatment of brain tumor. 5-FU-Ioaded PLGA microparticles were characterized by scanning electron microscopy (SEM), powder X-ray diffraction (XRD), and differential scanning calorimetry (DSC). SEM observation of the 5-FU-Ioaded PLGA microparticles prepared by rotary solvent evaporation method showed that 5-FU was almost surrounded by PLGA and significant reduction of crystallinity of 5-FU was confirmed by XRD. In case of release profile of 5-FU from 5-FU-Ioaded PLGA wafer fabricated microparticles prepared by mechanical, mixing, the release profile of 5-FU followed near first order release kinetics. In contrast to the above result, release profile of 5-FU from 5-FU-loaded PLGA wafer fabricated microparticles prepared by rotary solvent evaporation method followed near zero order release kinetics. These results indicate that preparation method of the 5-FU-loaded PLGA microparticles to fabricate into wafers was contributed to drug release profile.