Journal
JOURNAL OF ALLOYS AND COMPOUNDS
Volume 630, Issue -, Pages 133-145Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.12.240
Keywords
WO3; Spray pyrolysis; Doping; Solution surface tension; Fermi level; Opto-electronic properties
Categories
Funding
- Sectoral Operational Programme Human Resources Development (SOP HRD) [ID59321]
- European Social Fund
- Romanian Government
Ask authors/readers for more resources
In this paper we compare the optical and electrical properties of the WO3 thin films containing 2, 5 and 10 at.% of Ti and Mo additives, deposited by spray pyrolysis. The influence of the type and additive concentration on the nanostructure, topography and composition of the WO3 layers are mainly related to the surface tension energy changes, and further correlated with the (photo) electrical and optical properties. The FTO/WO3 junction through its characteristic, namely barrier height, ideality factor, flat band potential, and series resistance, served as a tool for associating the before mentioned characteristics. The morphology of the WO3 thin films densifies and the roughness is reduced with increasing Ti and Mo concentration, in good agreement with solution surface tension reduction. WO3 based films exhibit a p-type semiconducting behavior, as confirmed also by the Mott-Schottky analysis, with a lower p-type conductivity for the Ti-WO3 films, as higher number of oxygen vacancies are generated by Ti addition. Changes in conductivity are mainly attributed to the oxygen vacancies concentration evolution at the film surface due to oxygen/water adsorption. For heavily doped WO3 thin films the contribution of these surface processes to the overall conductivity is reduced since surface reactivity is lost by densification. As opposed to Ti-doping which has a detrimental effect on layers structure, Mo addition, even in high concentrations, has a positive effect on layers crystallinity; hence higher conductivity and ideality factors close to 1 are obtained for these films. Surprisingly, Ti and Mo-WO3 films contain cation additives also in lower oxidation states, 3+ and 5+, respectively, compared to the ones in the precursor salt. A 2 at.% Ti concentration is enough to significantly improve the photoconductivity of the WO3 films, whereas for Mo addition higher levels are needed (10 at.%). The Ti and Mo-WO3 films have high transparency with average transmission values of 85% and 75%, respectively. The thin films reflectance decreases with increasing doping concentration along with roughness diminution. (C) 2015 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available