JOURNAL OF ALLOYS AND COMPOUNDS
Volume 618, Issue -, Pages 533-536Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2014.08.254
Keywords
DMSs; GaN:Er; Room-temperature ferromagnetism
Categories
Funding
- National Natural Science Foundation of China [60876004]
Ask authors/readers for more resources
Er+ ions were implanted into the n-type, unintentionally-doped (u-type) and p-type GaN epilayers, respectively. Subsequent rapid thermal annealing process was carried out at 800 degrees C in N-2 ambience for 5 min. It is found that the micro-structure of GaN:Er films have a close relationship with the implantation and annealing process. Four new Raman peaks were introduced by Er+ ions implantation at 300, 362, 670 and 855 cm(-1), respectively. All the samples exhibit room-temperature ferromagnetism, which can be well explained by the bound magnetic polaron theory. Our experiments also revealed that the magnetic properties of GaN:Er samples are closely related to their conduction type and initial carrier concentration, and the magnetic coupling between the magnetic moments of Er3+ ions and electrons is stronger than that with holes. (C) 2014 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available