BIOMATERIALS
Volume 24, Issue 15, Pages 2623-2629Publisher
ELSEVIER SCI LTD
DOI: 10.1016/S0142-9612(03)00067-X
Keywords
calcium phosphate coating; RF magnetron sputtering; in vivo; roughness
Ask authors/readers for more resources
RF magnetron sputter deposition was used to produce 0.1, 1.0 and 4.0 mum thick Ca-P coatings on TiO2-blasted titanium discs. Half of the as-sputtered coated specimens were subjected to an additional infrared heat treatment for 30 s at 425-475degreesC. X-ray diffraction demonstrated that infrared radiation changed the amorphous 4 mum sputtered coatings into an amorphous-crystalline structure, while the amorphous 0.1 and 1 mum changed in a crystalline apatite structure with the presents of tetracalciumphosphate as a second phase. Scanning electron microscopically examination of the sputtered coatings revealed that annealing of the 4 mum thick coatings resulted in the appearance of small cracks. Subsequently, the discs were implanted subcutaneous into the back of rabbits. After 1, 4, 8 and 12 weeks of implantation, the implants were retrieved and prepared for histological and physicochemical evaluation. Histological evaluation revealed that the tissue response to all coated implants was very uniform. A very thin connective tissue capsule surrounded all implants. The capsule was usually free of inflammatory cells. At the interface, there was a close contact between the capsule and implant surface and no inflammatory cells were seen. Physicochemical evaluation showed that the 0.1 and I mum thick amorphous coatings had disappeared within I week of implantation. On the other hand, the 4 mum thick amorphous phase disappeared during the implantation periods, which was followed by the precipitation of a crystalline carbonate apatite. Further, at all implantation periods the heat-treated I and 4 pin thick coatings could be detected. Occasionally, a granular precipitate was deposited on the heat-treated 4 pm thick coating. Fourier transform infrared spectroscopy showed the formation of carbonate apatite (CO3-AP) on the 4 mum thick amorphous coating and on the heat-treated specimens. On basis of our findings, we conclude that I mum thick heat-treated Ca-P sputter coating on roughened titanium implants appear to be of sufficient thickness to show bioactive properties, under in vivo conditions. (C) 2003 Elsevier Science Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available