Influence of the molecular modifications on the properties of EPDM elastomers under irradiation

The degradation of the mechanical behaviour of EPDM elastomers used as cable insulation materials has been investigated by mechanical spectroscopy and tensile tests for different formulations: unvulcanised EPDM, vulcanised and stabilised elastorner with an antioxidant. In all cases, gamma-irradiation of EPDM under oxygen leads to a reduction of the molecular mobility indicated by the shift of the glass transition relaxation temperature towards higher temperatures. Moreover, the molecular flow occurring above T-g is suppressed after irradiation for the unvulcanised EPDM providing evidence of cross-linking. The competition between cross-linking and chain scissions is shown by the decrease of the storage modulus above the crystallites melting temperature (similar to40 degreesC) at doses larger than 100 kGy. A strong increase of the Young modulus and reduction of the elongation at break of the non-vulcanised EPDM becoming more brittle are shown by stress/strain characterisations performed at 80 degreesC. At the opposite vulcanised EPDM exhibits higher elongation at break after crystallites melting. This evolution is interpreted by the competition between cross-linking and chain scissions, being hindered by the crystallites at room temperature. The intrinsic irradiation effects can be isolated after crystallite melting. The reduction of the molecular mobility can be explained by a chemi-crystallisation process assisted by chain scissions, leading to a more rigid phase upon irradiation. (C) 2003 Elsevier B.V. All rights reserved.