The dependence of the rate of crosslinking in poly(dimethyl siloxane) on the thickness of coatings

dWe consider reasons why the crosslinking reaction rate in poly(dimethyl siloxane) (PDMS) network coatings might differ from the rate found in the bulk and specifically examine the influence of coating thickness. Infrared spectroscopic ellipsometry (IRSE) is employed as an in situ probe of the reactions between vinyl (-CH=CH2) end groups on PDMS and SiH groups in a crosslinker and between unreacted SiH groups and hydroxyl/silanol groups within PDMS coatings, all on silicon substrates. Measurements of the concentrations of SiH groups (using the characteristic vibration at 2160 cm(-1)) were obtained from coatings between 1 and 27 mum in thickness, over temperatures ranging from 25 to 120 degreesC. First-order kinetics are exhibited in the consumption of SiH groups. The reaction rate constant is found to decrease with increasing coating thickness. Although there is evidence that the Pt catalyst segregates to the interface with the substrate, this phenomenon does not appear to have an impact on the thickness dependence. The diffusion of water into the silicone might be the rate-limiting step in the reactions, however, and therefore lead to the observed thickness dependence of the reaction rate. (C) 2003 Elsevier Science Ltd. All rights reserved.