MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume 357, Issue 1-2, Pages 159-167Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/S0921-5093(03)00215-6
Keywords
Al-5 wt.% Fe alloy; severe plastic deformation; backpressure; ultrafine-grained structure
Ask authors/readers for more resources
A process for increasing both strength and ductility in a brittle Al-5 wt.% Fe alloy by Equal Channel Angular Pressing (ECAP) was investigated. The increase in solid solubility of iron in the Al matrix produced by intense deformation under ECAP permitted age hardening in this alloy although it is not hardenable by conventional processing. An ultrafine-grained microstructure of 325450 nm was obtained in a brittle, cast Al-5 wt.% Fe alloy by ECAP with various numbers of passes and backpressure levels from 40 to 275 MPa. A supersaturated solid solution with a maximum solubility of 0.6 wt.% of iron in an aluminium matrix was obtained during ECAP, which allowed ageing of the conventionally non-hardenable alloy. Strength, ductility and microhardness of the cast alloy processed by the ECAP technique were significantly enhanced (e.g. strength and ductility from 102 MPa and 3.4% to 261 MPa and 5.8%, respectively). The subsequent artificial ageing resulted in a further increase in strength to 272 MPa. It was shown by scanning electron microscopy (SEM) that the type of fracture of tensile specimens taken from material subjected to ECAP was predominantly ductile. An increase in backpressure retards cracking of intermetallic particles and enhances the workability and ductility of such alloys processed by ECAP. (C) 2003 Elsevier Science B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available