Journal
PHILOSOPHICAL MAGAZINE
Volume 83, Issue 35, Pages 3959-3976Publisher
TAYLOR & FRANCIS LTD
DOI: 10.1080/14786430310001616045
Keywords
-
Ask authors/readers for more resources
Carefully designed indentation creep experiments and detailed finite-element computations were carried out in order to establish a robust and systematic method to extract creep properties accurately during indentation creep tests. Samples made from an Al-5.3mol%Mg solid-solution alloy were tested at temperatures ranging from 573 to 773 K. Finite-element simulations confirmed that, for a power-law creep material, the indentation creep strain field is indeed self-similar in a constant-load indentation creep test, except during short transient periods at the initial loading stage and when there is a deformation mechanism change. Self-similar indentation creep leads to a constitutive equation from which the power-law creep exponent n, the activation energy Q(c) for creep, the back or internal stress and so on can be evaluated robustly. The creep stress exponent n was found to change distinctively from 4.8 to 3.2 below a critical stress level, while this critical stress decreases rapidly with increasing temperature. The activation energy for creep in the stress range of n = 3.2 was evaluated to be 123 W mol(-1), close to the activation energy for mutual diffusion of this alloy, 130 kJ mol(-1). Experimental results suggest that, within the n=3.2 regime, the creep is rate controlled by viscous glide of dislocations which drag solute atmosphere and the back or internal stress is proportional to the average applied stress. These results are in good agreement with those obtained from conventional uniaxial creep tests in the dislocation creep regime. It is thus confirmed that indentation creep tests of Al-5.3 mol% Mg solid-solution alloy at temperatures ranging from 573 to 773 K can be effectively used to extract material parameters equivalent to those obtained from conventional uniaxial creep tests in the dislocation creep regime.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available