Polymerization shrinkage: effects of constraint and filling technique in composite restorations

Objectives. To evaluate the linear polymerization shrinkage (LPS) and its effect upon mean gap width, bond strength and cohesive strength of a composite placed under different constraints (C-factors-CF) and fitting techniques. Methods. Composite was placed in cavities sized 4 x 4 x 2 mm(3) (CF = 3) or on flat dentin surfaces (CF = 0.3) of bovine incisors, after adhesive application. They were inserted in one or three increments, and light cured (600 mW/cm(2)) for 80 s. The LPS was measured by placing a probe on the top surface of the composite in order to measure its dislodgment in the top-bottom direction. Half of the sample was sectioned to obtain composite resin sticks subjecting them to tensile forces at 0.5 mm/min. The other half of the sample was sectioned and the mean gap width was measured in both sides of the sections. Then the sections were sliced again to obtain composite/dentin sticks. The mean gap width in the sticks was performed before subjecting them to tensile forces at 0.5 mm/min. Data was analyzed by a two-way ANOVA and the correlation between the bond strength and gap width was analyzed by simple linear regression. Results. (1) Linear polymerization shrinkage: significant differences were observed for the interaction (p < 0.05). Under the low constraint, the LPS were similar for both filling techniques. Under higher constraint, polymerization shrinkage was lower for the incremental technique. (2) Gap width and bond strength: no difference was detected either for interaction, or for technique (p > 0.05). Under higher constraint, the gap width was higher and the bond strength lower. (3) The cohesive strength of composite resin was similar for all groups (p > 0.05). No correlation between bond strength and gap width was found (p = 0.17). Significance. The effects of polymerization shrinkage were not reduced by the fitting technique under the different cavity constraints tested. (C) 2003 Academy of Dental Materials. Published by Elsevier Ltd. Alt rights reserved.