Roughness analysis of the cracked surfaces of a face centered cubic alloy

Intergranular and transgranular fracture surfaces obtained in a face centered cubic alloy are studied using 3D maps reconstructed by scanning electron microscopy stereo imaging. The roughness exponents measured in the intergranular and transgranular surfaces, respectively, zeta=0.83+/-0.05 and zeta=0.75+/-0.05, are in agreement with the universal roughness value of 3D fractures. However, the slightly smaller value related to the transgranular surface could be a consequence of crystallographic transgranular zones disseminated on the surface whose roughness exponent zeta=0.65+/-0.07 is close to the one usually measured on 2D fractures.