Surface fluorination of the cathode active materials for lithium secondary battery

LiMn2O4 was treated with F-2 at room temperature (RT), 373 and 473 K under 1.3, 6.6 and 13.2 kPa-F-2. XPS data indicate that two kinds of fluorine species may exist on the sample surface and the ratio of these fluorines is affected by choosing the reaction condition. The peak indicating Mnn+ bonded to fluorine appeared in the XPS spectra of Mn2p3/2 electron. From the results of the charge/discharge measurements, the efficiency of charge/discharge process for the sample fluorinated under 1.3, 6.6 and 13.2 kPa-F-2 below 373 K was larger than that of untreated one. The discharge capacity of the fluorinated sample was also larger than that of untreated one. The discharge capacity, the loss of discharge capacity during 50 charge/discharge cycles, F/O ratio measured from XPS data and the intensity of the peak indicating Mnn+ bonded to fluorine in the XPS spectra were closely related to each other. The optimal fluorination condition was under 1.3 kPa-F-2 at RT for 1 h. (C) 2004 Elsevier B.V. All rights reserved.