Nanoscale oxygen octahedral tilting in 0.90(Bi1/2Na1/2)TiO3-0.05(Bi1/2K1/2)TiO3-0.05BaTiO3 lead-free perovskite piezoelectric ceramics

The oxygen octahedral tilted domains in 0.90(Bi1/2Na1/2)TiO3-0.5(Bi1/2K1/2)TiO3-0.5BaTiO(3) lead-free perovskite piezoelectric ceramic have been studied by transmission electron microscopy (TEM). Selected-area electron diffraction patterns shows the 1/2ooo and 1/2ooe reflections, indicating the presence of antiphase (a(-)a(-)a(-)) and in-phase (a(o)a(o)c(+)) octahedral tilting, respectively. The morphology and distributions of these tilted domains are shown in the centered dark-field images. Further, the Bragg-filtered high-resolution TEM image reveals that the size of the in-phase tilted domains varies from 1 to 8 nm across. The ceramic contains the mixture of nontilted and variants of the antiphase and in-phase tilted domains. (C) 2009 American Institute of Physics. [DOI: 10.1063/1.3193544]