The local structure of two samples of vertically well-aligned ZnO nanorods with average diameters of 13 and 37 nm were studied using orientation-dependent x-ray absorption fine structure (XAFS) at the Zn K edge. The aligned ZnO nanorod samples were fabricated on sapphire (0001) substrates with a catalyst-free metalorganic vapor-phase epitaxy method. The XAFS measurements showed that both nanorod samples have a well-ordered wurtzite structure and that no vacancy was observed at either site of zinc or oxygen atoms. However, we found that in both samples the lattice constants of a and b were shrunken by similar to0.04 Angstrom while c was elongated by similar to0.1 Angstrom, compared with those of their bulk counterparts. Furthermore, there was a substantial amount of disorder in the bond length of the only Zn-O pairs located near the ab plane. This may suggest that the terminating atoms at the boundaries of the nanorods are oxygen atoms. (C) 2005 American Institute of Physics.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available