OXIDATION OF METALS
Volume 63, Issue 1-2, Pages 87-111Publisher
SPRINGER/PLENUM PUBLISHERS
DOI: 10.1007/s11085-005-1953-4
Keywords
erosion-corrosion; surface analysis; AES; XPS; particle strengthening
Categories
Ask authors/readers for more resources
Four steels (Fe2.25Cr1Mo, Fe9Cr1Mo, AISI 304, 353 MA) and one Ni-based superalloy (Inconel 625) were exposed in an erosion-corrosion test rig at the temperatures 20, 350, 550 and 700degreesC for 1 week. The atmosphere was air and the particle velocity 1.2 m/s. The composition and thickness of the developed surface layers were determined by Auger electron spectroscopy and X-ray photoelectron spectroscopy. The ferritic and Ni-based alloys investigated show a minimum in wastage rate around 350degreesC due to the development of a particle strengthened/toughened composite layer on the surface. The greatest wastage rates were measured at 700degreesC. Rapid diffusion paths created in the oxide from the particle bombardment results in the growth of oxide nodules at the oxide/metal-interface causing protruding oxide flakes which are chipped away. At this temperature the ferritic steel Fe9Cr1Mo is degraded to a larger extent than the austenitic steels.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available